Abstract:
Contamination of water sources by potentially toxic metal ions such as Cr(VI) is becoming a significant threat to many organisms. Among Cr compounds, Cr(VI) which exists as 𝐶𝑟𝑂42−, 𝐶𝑟2𝑂72−and 𝐻𝐶𝑟𝑂4− in aqueous media is a known potent carcinogen. Many technologies were adapted for the removal of Cr(VI) from aqueous solutions. Based on literature , pristine biochar has many limitations in removing Cr(VI). Mainly, pristine biochar has a negative surface charge which decreases the efficiency of adsorbing negative ionic species such as 𝐻𝐶𝑟𝑂4−. We developed a novel KOH-modified biochar/ Polypyrrole/ Al2O3 composite for the efficient removal of Cr(VI) ions. This work utilizes a simple synthesis method with minimal use of chemicals and experimental results suggest that this composite is a promising low-cost adsorbent of Cr(VI). The composite before and after removal of Cr(VI) was characterized by Scanning Electron Microscope(SEM), X-ray Diffraction Spectroscopy (XRD) and Fourier Transform Infra-Red Spectroscopy(FTIR). The removal of Cr(VI) in the aqueous phase was monitored by UV-Visible spectroscopy at 350 nm. pH, contact time, initial Cr(VI) ions concentration were optimized using batch adsorption method for the maximum removal of Cr(VI) ions. Composite exhibited maximum Cr(VI) removal percentage of 91.5% within 80 min at pH 2. It was found that percent removal efficiency increased from 73 to 91 when pH decreased from 8 to 2. The adsorption process between biochar composite and Cr(VI) reached an equilibrium within 80 minutes showing a rapid removal rate of over 73% within the first 20 minutes. Point of zero charge of composite was found to be about 4.0 and at pH less than 4.00, surface is positively charge which attracts negatively charge 𝐻𝐶𝑟𝑂4− electrostatically. The negative values of Δ𝐺° calculated at different temperatures indicate that the adsorption process is spontaneous at each temperature and positive Δ𝐻° value (36.36 kJ mol-1) shows that the adsorption process is endothermic. Δ𝐺° value increases with increase of temperature thus, spontaneity increases with temperature; indicated that adsorption of Cr(VI) was endothermic and spontaneous in nature. Isotherm data showed that the adsorption followed the Langmuir model where the maximum Langmuir adsorption capacity of composite was found to be 113.97 mg/g. In addition, a higher R2 value of 0.9923 obtained in the Langmuir model indicates that the surface of the adsorbent material is homogenous where the adsorption takes place via monolayer